Galvanized Steel
| Available Size | |
| Thickness ( mm ) | 0.23 ~ 2.30 |
| Width ( mm ) | 500 ~ 1,270 |
| Sheet Length ( mm ) | 600 ~ 5,000 |
| Coil Weight ( Max ) | 22.5 M/T |
| Coating Weight ( Both Sides ) | 76 ~ 720 g/m2 |
| Coil Inner Diameter ( mm ) | 508,610 |
Finishes
- Phosphatized
- Extra smooth (skin passed)
- Chemical treatment (chromated)
- Oiled
Designation and Mechanical Requirements Hot-Rolled base metal used
| Designation | Thickness mm | Yield Point min.N/mm2 | Tensile Strength mm.N/mm2 | Elongation min.% | Test Piece |
| SGHC | 1.6 ~ 6.0 | – | – | – | No. 5 Cut in Rolling Direction |
| SGH340 | 245 | 340 | 20 | ||
| SGH400 | 295 | 400 | 18 | ||
| SGH440 | 335 | 440 | 18 | ||
| SGH490 | 365 | 490 | 16 | ||
| SGH540 | 400 | 540 | 16 |
Cold-Rolled base metal used
| Designation | Thickness mm | Yield Point min. N/mm2 | Tensile Strength mm. N/mm2 | Elongation, min.% | Test Piece | |||||
| Nominal Thickness, min | ||||||||||
| 0.25 to 0.40 under | 0.40 to 0.60 under | 0.60 to 1.0 under | 1.0 to 1.6 under | 1.6 to 2.5 under | 2.5 and over | |||||
| SGCC | 0.25 ~ 3.2 | – | – | – | – | – | – | – | – | No. 5 Cut in Rolling Direction |
| SGCD1 | 0.40 ~ 2.3 | – | 270 | – | 34 | 36 | 37 | 38 | – | |
| SGCD2 | – | 270 | – | 36 | 38 | 39 | 40 | – | ||
| SGCD3 | 0.60 ~ 2.3 | – | 270 | – | 38 | 40 | 41 | 42 | – | |
| SGC340 | 0.25 ~ 3.2 | 245 | 340 | 20 | 20 | 20 | 20 | 20 | 20 | |
| SGC400 | 295 | 400 | 18 | 18 | 18 | 18 | 18 | 18 | ||
| SGC440 | 335 | 440 | 18 | 18 | 18 | 18 | 18 | 18 | ||
| SGC490 | 365 | 490 | 16 | 16 | 16 | 16 | 16 | 16 | ||
| SGC570 | 0.25 ~ 2.0 | 560 | 570 | – | – | – | – | – | – |
Weight of Zinc Coating
| Zinc Coating Designation | Z08 | Z10 | Z12 | Z18 | Z20 | Z22 | Z25 | Z27 | Z35 | Z45 | Z60 |
| Minimum Weight of Zinc Coating (g/m2) | 80 | 100 | 120 | 180 | 200 | 220 | 250 | 275 | 350 | 450 | 600 |
Remarks
The minimum weight of zinc coating mentioned above indicates the minimum weight of zinc coating on both sides of sheets or coils. This expresses the average measured weight of zinc coating of triple spot test pieces cut from the test sheets.
Pre-painted Galvanized Steel
Resistance to acid rain:
Coating protection mechanism: it is very easy to form acid rain in the high level of industrial emissions or pollutants environment. Acidic penetration is formed in the surface of pre-painted steel, and accelerates the corrosion, forming blistering, peeling and so on.
Resistance ultraviolet rays:
Coating protecting mechanism: pre-painted sheet in ultraviolet or strong sunlight conditions, the coating will exhibit chalking degeneration, manifested as discoloration and loss of gloss, lose paint quickly.
Resistance to humid heat:
Coating protecting mechanism: in hot and humid environments, high osmotic pressure of water vapor accelerates penetration, forming the degeneration of painting film, then the corrosion of the substrate, with the phenomenon of bubbles and peeling.
Resistance to low temperature:
Coating protecting mechanisms: most of the paint can keep stable processing performance above 0°degree, but at alpine region, the temperature will be below 20°-40°degrees, normal paint will become brittle bend cracking, or even lose paint, thus protection function is lost totally.
| Available Size | |
| Thickness (mm) | 0.20 ~ 3.20 |
| Width (mm) | 1,270 |
| Sheet Length (mm) | 600 ~ 5,000 |
| Coil Weight (Max) | 15 M/T |
| Coil inner diameter (mm) | 508/610 |
Available base metal
Galvanized steel sheet / Electrolytic galvanized steel sheet / Cold Rolled steel sheet / Galvalume steel sheet
Available Products
Regular polyester / Silicon modified polyester / Acrylic-sol / P.V.C. film / P.V.D.F
PVF film lamination / High polymer / Printed / Metal embossed
Powder Coated Products
Unlike the traditional liquid (wet) coat paint, the powder coat paint does not contain any unnecessary environmentally hazardous materials and is 100% solid (dry) paint. Various coating method is use to cover which then goes through the heat-fuse-harden process to produce the highest quality products.
Epoxy Polyester Coated Steel Sheets
Manufacturing Method: Electrostatic powder spraying on the coil surface one coat one bake using epoxy polyester powder resin.
●Material: CR, EGI, GI, GA, AL, SUS
● Film thickness: Front side – Top 35 ~ 70μ ( powder ) Back side – Top 5 ~ 10μ (wet )
Polyester Coated Steel Sheets
● Manufacturing Method : Electrostatic powder spraying one coat and one bake using polyester powder paint.
● Material : CR, EGI, GI, GA, AL, SUS
● Film thickness : Front side – Top 35 ~ 70μ
Back side – Bare or Top 5 ~ 10μ
Polyurethane Coated Steel Sheets (P.C.M sheet)
● Manufacturing Method: Electrostatic powder spraying on the coil surface one coat one bake using epoxy polyester powder resin.
● Material: CR, EGI, GI, GA, AL, SUS
● Film thickness: Front side – Top 25 ~ 75μ (controlled)
Back side – Bare or Top 5 ~ 10μ
Epoxy Coated Steel Sheets
● Manufacturing Method : Same as polyurethane.
● Material : CR, EGI, GI, GA, AL, SUS
● Film thickness : Front side – Top 25 ~ 70μ
Back side – Top 5 ~ 10μ
Liquid (Wet) Coated Products ( Coil or sheet products )
Regular polyester Coated Steel Sheets
● Manufacturing Method : Painting and backing every 2 times using regular modified polyester resin.
● Material : CR, EGI, GI, AL, SUS
● Film thickness : Front side – Primer 5μ, Top 15 ~ 20μ
Back side – Top 5 ~ 10μ
● Characteristics : Corrosion resistance weather resistance variety and beauty of color.
Silicon modified polyester Coated Steel Sheets
● Manufacturing Method : Painting and backing every 2 times using silicon modified polyester resin.
● Material : CR, EGI, GI, AL, SUS
● Film thickness : Front side – Primer 5μ, Top 10 ~ 30μ
Back side – Top 5 ~ 10μ
● Characteristics : Super corrosion resistance
Super weather resistance
Heat resistance
Chemical resistance
High polymer polyester Coated Steel Sheets
● Manufacturing Method : Painting and backing every 2 times using high polymer polyester resin.
● Material : CR, EGI, GI, GA, AL, SUS
● Film thickness : Front side – Primer 5μ, Top 15 ~ 20μ
Back side – Top 5 ~ 10μ
● Characteristics : Excellent workability, excellent appearance, variety and beauty of color.
P.V.D.F Coated Steel Sheets
● Manufacturing Method : 2 coat 2 bake using polyvinylidene fluoride resin.
● Material : GI, GA, AL, SUS
● Film thickness : Front side – Primer 5 ~ 7μ, Top 25 ~ 30μ
Back side – Top 5 ~ 10μ
● Characteristics : Super corrosion resistance
Super weather resistance
Heat resistance
Metallic P.V.D.F Coated Steel Sheets
● Manufacturing Method : 3 coat, 3 backing using polyvinylidene fluoride resin with metallic paste.
● Material : GI, GA, AL, SUS
● Film thickness : Front side – Primer 5 ~ 7μ, Top 20 ~ 25μ
Back side – Top 5 ~ 10μ
● Characteristics : Excellent weather resistance
Excellent corrosion resistance
Excellent chemical resistance
Printed Steel Sheets
● Manufacturing Method : Painting and backing various designs with Gravure offset print on the pre-painted steel coil.
● Material : CR, EGI, GI, AL, SUS
● Film thickness : Front side – Primer 5μ, Top 15μ
Ink 2 ~ 3μ, Clear 5 ~ 10μ
Back side – Top 5 ~ 10μ
● Characteristics : Variety of design, beauty color, good workability